作业帮这是什么牌号的钢材,C % :0.04 max Si% :0.30 max Mn% :0.25 0.5 S% :0.050 max P% :0.045 max Ni% :0.30 max Cr% :0.30 max Cu% :0.30 max N% :0.0080 max UTS (MPa) :300 TO 540 Upper Yield Stress (Mpa) :185 min Elongation after fracture (%) :18
来源：学生作业帮助网 编辑：作业帮 时间：2024/05/04 20:44:13
这是什么牌号的钢材,C % :0.04 max Si% :0.30 max Mn% :0.25 0.5 S% :0.050 max P% :0.045 max Ni% :0.30 max Cr% :0.30 max Cu% :0.30 max N% :0.0080 max UTS (MPa) :300 TO 540 Upper Yield Stress (Mpa) :185 min Elongation after fracture (%) :18
这是什么牌号的钢材,
C % :0.04 max Si% :0.30 max
Mn% :0.25 0.5 S% :0.050 max
P% :0.045 max Ni% :0.30 max
Cr% :0.30 max Cu% :0.30 max
N% :0.0080 max
UTS (MPa) :300 TO 540
Upper Yield Stress (Mpa) :185 min
Elongation after fracture (%) :18
这是什么牌号的钢材,C % :0.04 max Si% :0.30 max Mn% :0.25 0.5 S% :0.050 max P% :0.045 max Ni% :0.30 max Cr% :0.30 max Cu% :0.30 max N% :0.0080 max UTS (MPa) :300 TO 540 Upper Yield Stress (Mpa) :185 min Elongation after fracture (%) :18
碳 C ：0.32～0.40硅 Si：0.17～0.37锰 Mn：0.50～0.80硫 S ：≤0.035磷 P ：≤0.035铬 Cr：≤0.25镍 Ni：≤0.25铜 Cu：≤0.25抗拉强度 σb (MPa)：≥530(54)屈服强度 σs (MPa)：≥315(32)伸长率 δ5 (%)：≥20断面收缩率 ψ (%)：≥45冲击功 Akv (J)：≥55冲击韧性值 αkv (J/cm2)：≥69(7)这个是35号钢的,我看45#的也能和这个差不多,不知道是要做什么.如果知道用来做什么,哪个部件就好办了.因为这个样的板材棒材都很多,而且可以调制的.